Eporex® HIPS 828
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Eternal Plastics Co., Ltd. |
| Trademark: | Eporex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QhuGlF_Eporex-HIPS-828.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eporex® HIPS 828 is a High Impact Polystyrene material. It is available in North America for injection molding. Important attributes of Eporex® HIPS 828 are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 13 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 56 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 21.5 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 50 | % | ASTM D638 |
| Flexural Modulus | 2250 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 53.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 91 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 76.1 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ARE-55D | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| Braskem PE LH-537 | Braskem | LLDPE | Braskem PE |
| DEXFLEX® 826HF-UV | LyondellBasell Industries | TPO (POE) | DEXFLEX® |
| FORMULA P COMP 6220 M1 Z | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| Karina BLACK PVC COMPOUND 920D48/1-CY-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |