DENITER 1010
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Vamp Tech |
| Trademark: | DENITER |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QgRqI5_DENITER-1010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 10% glass fiber reinforced, not Flame Retardant compound, good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.0 | % | |
| Across Flow | 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 80.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 9.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 50 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 203 | °C | ASTM D648A |
| Vicat Softening Temperature | 204 | °C | ASTM D1525 1 |
| RTI Elec | 235 | °C | UL 746 |
| RTI Imp | 235 | °C | UL 746 |
| RTI Str | 235 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 675 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 GF 30 GID | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Titalon® 1200GFT | Titan Plastics Compounds Co., Ltd. | Nylon 6 | Titalon® |
| ALCOM® PA66 910/1.1 CF10 PTFE10 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| BJB Polyurethane SP-82 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| K-Bin Rigid PVC KB-7101 | K-Bin, Inc. | PVC, Rigid | K-Bin Rigid PVC |