Edgetek™ ET9200-5006 FD NATURAL
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QgPSOv_Edgetek-ET9200-5006-FD-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Flow | 1.5 to 1.8 | % | |
| Across Flow : 23°C, 2.00 mm 1 | 1.2 to 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 4000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C, Injection Molded) | 66.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C, Injection Molded) | > 2.0 | % | ISO 527-2/5 |
| Flexural Modulus (23°C, Injection Molded) | 3900 | MPa | ISO 178 |
| Flexural Stress (23°C, Injection Molded) | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 2.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 30 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 115 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 95.0 | °C | ISO 75-2/C |
| Glass Transition Temperature | 90.0 | °C | ISO 11357-2 |
| Melting Temperature | 280 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 304 to 332 | °C |
| Note Message | |
|---|---|
| 1 . | Bergmann method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polypropylene C7020-20 ESU BG 33 | Trinseo | PP, Unspecified | Polypropylene |
| RTP 800 TFE 2 | RTP Company | Acetal (POM) Copolymer | RTP |
| Radilon® S CP300 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| Flontech® FT-BRR25-CF10-M5-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Plaslube® AC-80/SI/2 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |