PRL PPX/NY-GP1
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QgNQeg_PRL-PPX-NY-GP1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX/NY-GP1 is a Polyphenylene Ether + PS + Nylon (PPE+PS+Nylon) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/3.8 kg) | 20 to 40 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.90 to 1.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 57.9 | MPa | |
| Break, 3.18 mm | 55.2 | MPa | |
| Flexural Modulus (3.18 mm) | 2070 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 210 | J/m | ASTM D256 |
| Gardner Impact (3.18 mm) | 28.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 141 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 113 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | ||
| 3.18 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 to 107 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 260 to 299 | °C | |
| Middle Temperature | 271 to 299 | °C | |
| Front Temperature | 277 to 299 | °C | |
| Processing (Melt) Temp | 277 to 299 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 5613 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
| Tenite™ Propionate 383A2R30007 Natural, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| AKROMID® A3 GK 40 1 natural (1803) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| LEXAN™ HFR1723 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Primocon GC25A | KMI Group, Inc. | Acetal (POM) Copolymer | Primocon |