IROGRAN A 75 P 4655 N is a black colored polyether based thermoplastic polyurethane intended for injection moulding applications. IROGRAN A 75 P 4655 N is a part of the HUNTSMAN injection moulding product range. It is processable at low temperatures and offers a specially designed, flexible material suitable for mouldings. PERFORMANCE FEATURES
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.12 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (190°C/10.0 kg) | 50.0 | cm³/10min | |
| Molding Shrinkage - Flow (Injection Molded) | 0.80 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, DIN 53505 | ||
| Shore A, Injection Molded | 73 | ||
| Shore D, Injection Molded | 23 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | 60 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| TMA 3 | Internal Method | ||
| High : 635.0 µm | 155 | °C | |
| Low : 635.0 µm | 122 | °C |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 4 | DIN 53504 | ||
| 100% Strain, 0.635 mm | 5.80 | MPa | |
| 300% Strain, 0.635 mm | 9.00 | MPa | |
| Tensile Stress 5(Break, 0.635 mm) | 30.0 | MPa | DIN 53504 |
| Tensile Elongation 6(Break, 0.635 mm) | 820 | % | DIN 53504 |
| Tear Strength 7(0.635 mm) | 45 | kN/m | DIN 53515 |
| Compression Set 8 | ASTM D395, DIN 53517 | ||
| 23°C, 24 hr | 23 | % | |
| 70°C, 24 hr | 39 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Hot Air Dryer | 80.0 to 90.0 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Rear Temperature | 185 | °C | |
| Middle Temperature | 185 | °C | |
| Front Temperature | 185 | °C | |
| Nozzle Temperature | 185 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Extruded Film |
| 4 . | Extruded Film |
| 5 . | Extruded Film |
| 6 . | Extruded Film |
| 7 . | Extruded Film |
| 8 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Texalan® 4 Series 470A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 4 Series |
| Crastin® SK645FR NC010 | DuPont Performance Polymers | PBT | Crastin® |
| KRATON® G1640 E | Kraton Polymers LLC | SEBS | KRATON® |
| LNP™ THERMOCOMP™ Lexan_LGK3020 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| Geon™ Vinyl Rigid Molding M3530 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |