Vyncolit® GS84
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QeWaTm_Vyncolit-GS84.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit GS84 is a cotton filled phenolic moulding compound with excellent mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Apparent Density | 0.40 | g/cm³ | ISO 60 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 35.0 | MPa | ISO 527-2 |
| Flexural Modulus | 6750 | MPa | ISO 178 |
| Flexural Stress | 60.0 | MPa | ISO 178 |
| Compressive Stress | 150 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 150 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 10 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (4.00 mm) | V-1 | UL 94 |
| Additional Information |
|---|
| Apparent Density, ISO 60: 0.35 to 0.45 g/cm³Mold Shrinkage, ISO 2577: 0.60 to 0.80 %Post Shrinkage, ISO 2577: 0.60 to 0.80 %Flexural Modulus, ISO 178: 6 to 7.5 GPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 5531N-SI | TSRC Corporation | TPE | T-Blend® |
| Formolene® L62009B | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| Elastollan® 1190A10 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| Epocast 8623-A/Hardener 946 | Huntsman Advanced Materials | Epoxy | Epocast |
| ALFATER XL® A70I 4PA0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |