Order Products : sales@su-jiao.com
InnoPlus HD7000H
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QdqIZT_InnoPlus-HD7000H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
InnoPlus HD7000H is high density polyethylene which has outstanding mechanical strength, good weathering resistance and excellent product appearance. It is suitable to produce not only truck-bed liner from sheet extrusion and thermoforming process but also automotive fuel tanks from blow molding process. Typical Application: Truck-bed liner, Automotive fuel tank |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.10 | g/10 min | |
| 190°C/21.6 kg | 10 | g/10 min | |
| Environmental Stress-Cracking Resistance (25% Igepal, F50) | > 1000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 27.5 | MPa | |
| Break | 39.2 | MPa | |
| Tensile Elongation (Break) | 900 | % | ASTM D638 |
| Apparent Bending Modulus | 834 | MPa | ASTM D747 |
| Flexural Modulus | 1080 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | 460 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 126 | °C | ASTM D1525 2 |
| Peak Melting Temperature | 130 | °C | ASTM D3418 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blow Molding Temperature | 190 to 220 | °C | |
| Thermoforming Molding Temperature | 210 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | Non break |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® RCopo 1.8.CL | Marco Polo International, Inc. | PP Random Copolymer | MARPOL® RCopo |
| AIE PPO 9010F-SM20 | Asia International Enterprise (Hong Kong) Limited | PPE+PS | AIE PPO |
| Asrene® SI 5230 | Chandra Asri Petrochemical | HDPE | Asrene® |
| FORMOCON® FM270 | Formosa Plastics Corporation | Acetal (POM) Copolymer | FORMOCON® |
| EMERGE™ PC 8310-22 | Trinseo | PC | EMERGE™ |