Order Products : sales@su-jiao.com
LG ASA LI980
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QcaIVR_LGASALI980.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Description
Application
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 96 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 39.2 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, 3.20mm | > 6.0 | % | ASTM D638 |
| Fracture, 3.20mm | 70 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1730 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 68.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 80.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.6 mm | HB | UL 94 | |
| 3.2 mm | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Cylinder Zone 1 Temp. | 190 - 200 | °C | |
| Cylinder Zone 2 Temp. | 200 - 220 | °C | |
| Cylinder Zone 3 Temp. | 210 - 230 | °C | |
| Cylinder Zone 4 Temp. | 210 - 230 | °C | |
| Adapter Temperature | 210 - 230 | °C | |
| Melt Temperature | 200 - 230 | °C | |
| Die Temperature | 210 - 250 | °C |
| Extrusion instructions |
|---|
| Minimum Moisture Content: 0.01%Roll Stack Temperature, Top: 70 to 90°CRoll Stack Temperature, Middle: 70 to 90°CRoll Stack Temperature, Bottom: 70 to 100°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 GF 25 H | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| YUPLENE® BT3500 | SK Global Chemical | PP Impact Copolymer | YUPLENE® |
| BJB Polyurethane TC-890 FR REV 1 | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| CP PRYME® Polycarbonate PC100RULUV-10M Black | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| Hylon® N2015HL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |