Ultrason® E 2010 C6
| Category: | PESU , Polyethersulfone |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultrason® E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QbqciX_Ultrason-E-2010-C6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity injection moulding grade with high rigidity and strength, 30 % carbon fiber reinforced. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.80 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (360°C/10.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.35 | % | |
| Flow | 0.15 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.7 | % | |
| Equilibrium, 23°C, 50% RH | 0.60 | % | |
| Viscosity Number 1 | 56.0 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 227 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 22000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 185 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.5 | kJ/m² | |
| 23°C | 7.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 225 | °C | ISO 75-2/A |
| Glass Transition Temperature 2 | 225 | °C | ISO 11357-2 |
| CLTE - Flow | |||
| 23 to 80°C | 4.0E-6 | cm/cm/°C | ISO 11359-2 |
| 180°C | 4.0E-6 | cm/cm/°C | DIN 53752 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms | IEC 60093 |
| Volume Resistivity 3 | 1.9 | ohms·cm | ISO 3915 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 350 | °C | |
| Middle Temperature | 360 | °C | |
| Front Temperature | 370 | °C | |
| Nozzle Temperature | 370 | °C | |
| Processing (Melt) Temp | 350 to 390 | °C | |
| Mold Temperature | 150 to 190 | °C | |
| Screw Speed | < 300 | mm/sec |
| Note Message | |
|---|---|
| 1 . | in 0,01 g/ml Phenol/1,2, ortho-Dichlorbenzol, 1:1 |
| 2 . | 10°C/min |
| 3 . | 4 point method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTAMID® Terra DS16-GF30 | Evonik Industries AG | Nylon 1010 | VESTAMID® Terra |
| Vital-Line SHE5240G | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Unipren® Elastomers B3 PRTA010 45A UP313 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| Yuyao PPO GFN3-701 | Yuyao Tenglong Plastics Co., Ltd. | PPE+PS | Yuyao PPO |
| Plexiglas® DRM2-101 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |