Petro Rabigh PP AW564
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Rabigh Refining & Petrochemical Co. |
| Trademark: | Petro Rabigh PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QaKeuZ_Petro-Rabigh-PP-AW564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AW564 is a block copolymer polypropylene intended for industrial application. It is formulated with nucleating agent to enhance the stiffness. Injection molding parts made from this resin exhibit good impact, high stiffness and good heat stability. Applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow | 1.4 | % | |
| Across Flow | 1.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 96 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 28.0 | MPa | |
| Break | 15.0 | MPa | |
| Flexural Modulus | 1530 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ASTM D256 | ||
| -20°C | 5.0 | kJ/m² | |
| 23°C | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 124 | °C | ASTM D648 |
| Vicat Softening Temperature | 153 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tectron E1199 | TECTRON Systems Pte Ltd | TPV | Tectron |
| Stanyl® TW241F3 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| VAMPLEN 1025 V2 | Vamp Tech | PP Homopolymer | VAMPLEN |
| Daelim Po1y® PP-180 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| SABIC® HDPE CC2056 | Saudi Basic Industries Corporation (SABIC) | HDPE Copolymer | SABIC® HDPE |