Nypol® PA A3 BRC0001 NR349
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QZt2Ky_Nypol-PA-A3-BRC0001-NR349.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 66 in color white, with good set of mechanical properties, good set of thermal properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.14 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.5 to 2.0 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.3 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | 104 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 85.0 | 61.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | 40 | % | ASTM D638 |
| Flexural Modulus | 2750 | 1800 | MPa | ASTM D790 |
| Flexural Strength | 100 | 65.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 50 | 60 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 65.0 | -- | °C | ASTM D648 |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | 1.0E+13 | ohms·cm | ASTM D257 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 0.5.NB | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |
| SCHULAMID® 612 GF 30 HI | A. Schulman Europe | Nylon 612 | SCHULAMID® |
| Nylene® 5133 HS | Custom Resins Group | Nylon 66 | Nylene® |
| Grilamid® L XE 4074 black 9225 | EMS-GRIVORY | Nylon 12 | Grilamid® |
| Starex VH-0815 M | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |