ACLAR® UltRx 2000
| Category: | PCTFE , Polychlorotrifluoroethylene |
| Manufacturer: | Honeywell |
| Trademark: | ACLAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QXg4cb_ACLAR-UltRx-2000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aclar UltRx 2000 is a 2.00 mil PCTFE homopolymer, high performance barrier film for the pharmaceutical and medical markets. It thermoforms well on conventional blister packaging equipment and provides the best barrier of any clear film. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.10 | g/cm³ | ASTM D1505 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD : 51 µm | 1170 | MPa | ASTM D882 |
| TD : 51 µm | 1170 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 52.0 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 41.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 51 µm | 200 | % | ASTM D882 |
| TD : Yield, 51 µm | 250 | % | ASTM D882 |
| Water Vapor Transmission Rate | ASTM F1249 | ||
| 50 µm, 40°C, 75% RH | 0.10 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 50 µm, 38°C, 100% RH | 0.12 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 50 µm, 25°C, 60% RH | 0.019 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 50 µm, 30°C, 60% RH | 0.039 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.8 µm) | 1.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield, No Standard: 9.34 m²/kgTensile Strength @ Yld, ASTM D882, MD, 2 mil: 7000 to 10000 psiTensile Strength @ Yld, ASTM D882, TD, 2 mil: 4500 to 7500 psiTensile Elongation @ Yield, ASTM D882, MD, 2 mil: 150 to 200%Tensile Elongation @ Yield, ASTM D882, TD, 2 mil: 175 to 250%Secant Modulus, ASTM D882, 2 mil, MD & TD: 170000 to 200000Crystalline Melting Point, ASTM D4591: 211 °CDimensional Stability, ASTM D1204, MD: /= 42 dynes/cm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALTECH® PA6 A 2050/100 GF50 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| APEX® 90-A481R-75-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| ExxonMobil™ LDPE LD 103 Series | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| POLYfill PPH T20040 | Polykemi AB | PP Homopolymer | POLYfill |
| Kepital® F10-01 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |