Biocycle 189D-1
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | Biocycle |
| Trademark: | Biocycle |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QXY4Yu_Biocycle-189D-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Characteristics of the product: Yellowish white powder, with a high degree of purity of over 99.5% and humidity below 0.3%. Weight-average molecular weight of approximately 600,000 g/mol. Basic Raw Material: Saccharose Microorganism: Bacteria of the alcaligene genus Obtention Process: Biosynthesis of the polymer by aerobic fermentation and extraction purification of the polymer through natural solvent. Advantages: The polymer is totally biodegradable and renewable with its final decomposition in water and carbon dioxide through the action of microorganisms in natural environment; When placed in composting units, the polymer quickly decomposes and doesn't affect the quality of the compost produced. The polymer can be dyed by using biodegradable masterbatches in conventional dying processes. The polymer can be printed with paints and conventional printing processes, using surface treatment which are also conventional. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 36.0 | MPa | ASTM D638 |
| Yield | 38.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 3800 | MPa | ASTM D790 |
| -- | 3850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -- | 34 | J/m | ISO 180/A |
| -- | 36 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 125 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 123 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 74.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 137 | °C | ASTM D1525 |
| -- | 136 | °C | ISO 306/A120 |
| Peak Melting Temperature | 165 to 170 | °C | ASTM D3418 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rulon® 488 | Saint Gobain Performance Plastics | PTFE | Rulon® |
| BR® 127 | Cytec Industries Inc. | Epoxy | BR® |
| DURANEX® 2002U | Polyplastics Co., Ltd. | PBT | DURANEX® |
| LNP™ THERMOCOMP™ SF008 compound | SABIC Innovative Plastics | Nylon 12 | LNP™ THERMOCOMP™ |
| LNP™ LUBRILOY™ RF208 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |