Isocor™ 4011
| Category: | Nylon 6/69 , Polyamide 6/69 Copolymer |
| Manufacturer: | Shakespeare Monofilaments and Specialty Polymers |
| Trademark: | Isocor™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QXQKYG_Isocor-4011.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Isocor™ 4011 is a high viscosity PA-6/69. This resin is specifically suited for applications requiring superior toughness and abrasion resistance. Isocor™ 4011 is also used in applications requiring good electrical insulation properties. This resin can be processed using conventional techniques. Typical applications for 4011 include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.12 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.4 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 3.7 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D) | 79 | -- | ASTM D2240 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 39.3 | 33.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 300 | 390 | % | ASTM D638 |
| Flexural Modulus | 634 | 407 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 160 J/m | No Break | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 141 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 42.2 | -- | °C | ASTM D648 |
| Melting Temperature | 200 | -- | °C | DSC |
| Injection | Dry | Unit | |
|---|---|---|---|
| Dew Point | < -17.8 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Hopper Temperature | 79.4 | °C | |
| Rear Temperature | 216 - 238 | °C | |
| Middle Temperature | 221 - 254 | °C | |
| Front Temperature | 232 - 266 | °C | |
| Nozzle Temperature | 232 - 266 | °C | |
| Processing (Melt) Temp | 232 - 266 | °C | |
| Mold Temperature | -6.67 - 93.3 | °C | |
| Injection Pressure | 3.45 - 13.8 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.689 | MPa |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.10 | % | |
| Hopper Temperature | 79.4 | °C | |
| Cylinder Zone 1 Temp. | 263 | °C | |
| Cylinder Zone 2 Temp. | 263 | °C | |
| Cylinder Zone 3 Temp. | 268 | °C | |
| Cylinder Zone 4 Temp. | 268 | °C | |
| Die Temperature | 254 | °C |
| Extrusion instructions |
|---|
| Flange: 500°F (260°C)Air Dew Point (max): 0°F (-18°C)Neck: 500°F (260°C)Head: 500°F (260°C)Pump: 500°F (260°C)L/D Ratio: 24 to 30:1Compression Ratio: 3.5:1Polymer @ Die: 450°F (232°C)Screw Pressure: 2000 psi |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EVICOM™ GA4/130 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| DINAPLEN® PPH1S20 M403 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| Escorene™ Ultra LD 713.93 Molding | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Karina BLACK PVC COMPOUND 600D48/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8376-92UV Yellow 4209 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |