Order Products : sales@su-jiao.com
UNITHENE® LH523
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | USI Corporation |
| Trademark: | UNITHENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QWkCWd_UNITHENE-LH523.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UNITHENE LH523 is a high density polyethylene (HDPE) especially developed for injection molding. In addition, it can be applied to powder coating after grinding. High melt index of UNITHENE LH523 makes it exhibit excellent processability. Also, UNITHENE LH523 possesses superb impact strength and resistance to stress crack owing to its lower density. LH523 can be easily pigmented to any color by either dry blending or melt blending of the pigment into the resin. The products of LH523 can be easily printed after flame, chemical or electronic surface treatment. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 23 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 68 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 1% Secant (Compression Molded) | 745 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 22.6 | MPa | ASTM D638 |
| Fracture | 28.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 300 | % | ASTM D638 |
| Apparent Bending Modulus | 804 | MPa | ASTM D747 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 34 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Peak Melting Temperature | 132 | °C | ASTM D3418 |
| Additional Information |
|---|
| Torsional Stiffness, ASTM D1043: 9200 kg/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 202 RC HS Black | RTP Company | Nylon 66 | RTP |
| Mylar® WC (48 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Celanex® 1400FC | Celanese Corporation | PBT | Celanex® |
| Durethan® BKV 60 XF 900116 | LANXESS GmbH | Nylon 6 | Durethan® |
| LNP™ THERMOCOMP™ DX11355 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |