AXELERON™ FO 6549 NT CPD
| Category: | MDPE , Colorable Medium Density Polyethylene Compound for Cable Jacketing |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AXELERON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QWYoHP_AXELERON-FO-6549-NT-CPD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AXELERON™ FO 6549 NT CPD is a medium-density polyethylene compound ("CPD") designed for communications and power cable jacket use. It provides good electrical properties' processability combined with toughness, and stress crack resistance. Specifications AXELERON™ FO 6549 NT CPD meets the following raw material specifications:
|
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.935 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal, F0) | > 500 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 27.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1000 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -100 | °C | ASTM D746 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 - 227 | °C |
| Extrusion instructions |
|---|
| Melt extrusion temperatures in the range of 400-440°F are suggested for AXELERON™ FO 6549 NT CPD. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PBT T1306 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PBT | Nanjing Hongrui PBT |
| ADDINYL A2 I | ADDIPLAST | Nylon 66 | ADDINYL |
| APEX® 96-A0097D-85 | Teknor Apex Company | PVC, Flexible | APEX® |
| Kemcor MD 0898 | Qenos Pty Ltd | MDPE | Kemcor |
| LG EVA EP28025 | LG Chem Ltd. | EVA | LG EVA |