| Category: | PEI , Polyether Imide |
| Manufacturer: | Nanjing Lihan Chemical Co., Ltd. |
| Trademark: | LIHAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QVQtRQ_LIHAN-I706.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass fiber reinforced Polyetherimide Pamphlet: The polyetherimide has high mechanical strength and excellent heat resistance. The relative thermal index (RTI) for 30wt% glass fiber reinforced PEI material has reached 180°C. The material can be used to automotive parts, fasters around automobile engines and high current circuit breaker. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 to 0.60 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 160 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 9000 | MPa | ISO 178 |
| Flexural Stress | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 9.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 325 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 290 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Comparative Tracking Index | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 360 to 410 | °C | |
| Mold Temperature | > 130 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 66 A12^ F25 FR6 | Polykemi AB | Nylon 66 | SCANAMID 66 |
| SLOVAMID® 66 GF 35 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Karina IVORY PVC COMPOUND 105852-35/1-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ RF004XXD compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Plexiglas® V045 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |