Fiberfil® PP-60/V2
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QTzNR6_Fiberfil-PP-60-V2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil®PP-60/V2 is a polypropylene homopolymer (PP Homopoly) material,. This product is available in North America,. Fiberfil®The main features of PP-60/V2 are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 1.7 - 2.0 | % | ASTM D955 |
| 6.35 mm | 2.0 - 2.5 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 - 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1550 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 37.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 15 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 1480 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 42.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 82.2 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 76.7 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 182 - 199 | °C | |
| Middle Temperature | 193 - 210 | °C | |
| Front Temperature | 188 - 204 | °C | |
| Nozzle Temperature | 182 - 193 | °C | |
| Processing (Melt) Temp | 193 - 216 | °C | |
| Mold Temperature | 32.2 - 71.1 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw speed: Slow to Medium |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-2683B | Teknor Apex Company | TPO (POE) | Telcar® |
| DINALON® PA 6 ESPECIAL IMPACTO MEDIO | Grupo Repol | Nylon 6 | DINALON® |
| Genestar™ N1001D-U83/02 | Kuraray Co., Ltd. | Nylon 9T | Genestar™ |
| Karina GREEN COLOR CONCENTRATE 40/ 67-FC-LMP (SDB) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLUSTEK PA352M6 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |