TECACOMP® PEEK 150 CF30 black 3154
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QTdAco_TECACOMPPEEK150CF30black3154.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | |
| Apparent Density | 0.63 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (360°C/2.16 kg) | 4.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (360°C/2.16 kg) | 3.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.57 | % | ISO 294-4 |
| Flow | 0.19 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 25000 | MPa | ISO 527-2/50 |
| Tensile Stress | 240 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 38 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 335 | °C | ISO 75-2/A |
| Glass Transition Temperature | 143 | °C | DIN 53765 |
| Melting Temperature | 343 | °C | DIN 53765 |
| Service Temperature | |||
| long term | 260 | °C | |
| short term | 300 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electrical Conductivity | 8.66 | S/m | DIN EN 61340 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 - 160 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 360 - 400 | °C | |
| Mold Temperature | 160 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN2720SN | Ginar Technology Co., LTD. | Nylon 66/6 | Mapex |
| Formolene® L62608 | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| Generic MAH-g | Generic | MAH-g | Generic |
| LNP™ LUBRICOMP™ DFP36 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| LUVOCOM® 1105-0779/WT | Lehmann & Voss & Co. | PEEK | LUVOCOM® |