RTP 2740 U-50A
| Category: | SBS , Styrene Butadiene Styrene Block Copolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QQBm6f_RTP-2740-U-50A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 2.5 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 3.14 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 370 | % | ASTM D638 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 149 to 199 | °C | |
| Middle Temperature | 149 to 199 | °C | |
| Front Temperature | 149 to 199 | °C | |
| Mold Temperature | 10.0 to 40.6 | °C | |
| Injection Pressure | 3.45 to 6.89 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 227 MS | RTP Company | Nylon 66 | RTP |
| New-prene™ 9175N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| DIOSHY® TPEE E940D-HD | DIOSHY Co.,Ltd. | TPEE | DIOSHY® |
| Globalene® 73F4-2 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| LITEN FB 29 | UNIPETROL RPA | PE Copolymer | LITEN |