LEXAN™ HFD1810 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QQBHE9_LEXAN-HFD1810-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40 MFR LEXAN High Flow Ductile Copolymer |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 40 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 38.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2270 | MPa | ASTM D638 |
| -- | 2180 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Break 3 | 56.0 | MPa | ASTM D638 |
| Break | 56.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.5 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 130 | % | ASTM D638 |
| Break | 97 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2240 | MPa | ASTM D790 |
| -- 7 | 2180 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 91.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 64 | kJ/m² | |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 110 | J/m | ASTM D256 |
| 0°C | 700 | J/m | ASTM D256 |
| 23°C | 730 | J/m | ASTM D256 |
| -30°C 11 | 11 | kJ/m² | ISO 180/1A |
| 23°C 12 | 58 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 13 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 56.0 | J | ASTM D3763 |
| -- | 95.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 121 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 14 | 115 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 135 | °C | ASTM D1525 15 |
| -- | 129 | °C | ISO 306/B50 |
| -- | 130 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.0E-5 | cm/cm/°C | |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI Str | 105 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.300 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.582 | ASTM D542 | |
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | < 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 238 to 282 | °C | |
| Middle Temperature | 249 to 293 | °C | |
| Front Temperature | 260 to 304 | °C | |
| Nozzle Temperature | 254 to 299 | °C | |
| Processing (Melt) Temp | 260 to 304 | °C | |
| Mold Temperature | 48.9 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 35 to 75 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 80*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenopom® POM B3 HF NTLA010 PR306 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| VeroClear™ RGD810 | Stratasys | Unspecified | VeroClear™ |
| Tool-A-Thane UT-605 | Urethane Tooling & Engineering Corp | PUR, Unspecified | Tool-A-Thane |
| DOW™ LDPE 601C | The Dow Chemical Company | LDPE | DOW™ LDPE |
| SQUARE® SFR1970-70 | Shenzhen SQUARE Silicone Co., Ltd. | Fluoro Si | SQUARE® |