Terluran® EGP-7
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Terluran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QMZzx2_Terluran-EGP-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Terluran EGP-7 is an extrusion grade with well balanced properties. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Apparent Density | 0.55 - 0.65 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.95 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.21 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 97.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 43.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 2.9 | % | ISO 527-2 |
| Flexural Modulus | 2000 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 14 | kJ/m² | ISO 179 |
| 23°C | 33 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 | |
| Notched Izod Impact | ISO 180/A | ||
| -30°C | 14 | kJ/m² | ISO 180/A |
| 23°C | 34 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, annealed | 103 | °C | ISO 75-2/B |
| 1.8 MPa, annealed | 101 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 107 | °C | ISO 306/A50 |
| -- | 100 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 - 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.17 | W/m/K | DIN 52612 |
| Maximum Service Temperature | 80 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 203 - 250 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer S71U | Precision Polymer Engineering Ltd. | Silicone | Precision Polymer |
| Sevrite™ 3000-85A | Vi-Chem Corporation | TPE | Sevrite™ |
| VALOX™ 310 resin | SABIC Innovative Plastics | PBT | VALOX™ |
| CEFOR™ 1210P | The Dow Chemical Company | LLDPE | CEFOR™ |
| LNP™ THERMOCOMP™ OF008 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ THERMOCOMP™ |