PROTEQ™ GC30H255
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | PROTEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QM7YDv_PROTEQ-GC30H255.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PROTEQ™ GC30H255 is a 30% coupled glass fibre reinforced homopolymer polypropylene compound. This grade has a combination of high stiffness and tensile strength coupled with high impact strength and contains stabilisers for metal deactivation and heat resistance. These properties give the material excellent creep resistance and long term durability as well as high physical strength. Typical applications are automotive fans and fan shrouds. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 79 | ||
| Shore D, 15 sec | 73 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 80.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 5500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 70 | J/m | |
| 0°C, 3.20 mm | 75 | J/m | |
| 23°C, 3.20 mm | 80 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 155 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 145 | °C | |
| Vicat Softening Temperature | 160 | °C | ASTM D1525 4 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 215 to 235 | °C | |
| Middle Temperature | 235 to 255 | °C | |
| Front Temperature | 245 to 275 | °C | |
| Processing (Melt) Temp | 230 to 280 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Injection Pressure | 160 to 250 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 10 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Texalan® 2 Series 285A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 2 Series |
| NILSAN S MR K17V | Taro Plast S.p.A. | ABS | NILSAN |
| DESLON™ 66 DSC211GM | DESCO Co., Ltd. | Nylon 66 | DESLON™ 66 |
| Grivory® HTV-6H1 black 9205 | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| Sylvin 9915-90 Green 3160 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |