PRL PPX/NY-G10
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QKXEiv_PRL-PPX-NY-G10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PRL PPX/NY-G10 is a Polyphenylene Ether + PS + Nylon (PPE+PS+Nylon) product filled with 10% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: rohs compliant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/3.8 kg) | 2.0 to 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 86.2 | MPa | |
| Break, 3.18 mm | 86.2 | MPa | |
| Flexural Modulus (3.18 mm) | 3520 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 141 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 204 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 216 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 to 107 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 268 to 302 | °C | |
| Middle Temperature | 274 to 302 | °C | |
| Front Temperature | 279 to 302 | °C | |
| Processing (Melt) Temp | 279 to 302 | °C | |
| Mold Temperature | 79.4 to 121 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-2090-30A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Softflex® 5500 | Network Polymers, Inc. | TPE | Softflex® |
| Andur M-11 (94% 1,4BD, 6% TMP) | Anderson Development Company | PUR-Ester/MDI | Andur |
| Sylvin 9077-75 Grey 9516 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ 103R resin | SABIC Innovative Plastics | PC | LEXAN™ |