Modified PPE PA/PPE alloy 20% Filler reinforced Non-Flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1(3.00 mm) | 0.30 to 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 5600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 12 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 180 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 65°C) | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 7.1E+15 | ohms·cm | IEC 60093 |
| Electric Strength 3(2.00 mm) | 38 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.50 | ||
| 1 MHz | 3.30 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 8.0E-3 | ||
| 1 MHz | 0.012 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 130 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 300 | °C | |
| Mold Temperature | 60.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 120x80x3 mm |
| 2 . | 4 mm |
| 3 . | Short Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PPH-30T Nat | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| PrimoPrene 70A-1000 | KMI Group Inc. | TPV | PrimoPrene |
| RABALON® MJ7301C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| Zytel® 70G50HSLA BK039B | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Nypol® PA B3 G35 HS PRTA011 NT391 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |