| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | QTR, Inc. |
| Trademark: | QR Resin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QIiIBx_QR-Resin-QR-1230.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| QR-1230 is availible with UV (V) or Release (R). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/3.8 kg | 6.0 | g/10 min | |
| 260°C/5.0 kg | 30 | g/10 min | |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 55.8 | MPa | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 121 | °C | |
| 1.8 MPa, Unannealed | 104 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 246 to 277 | °C | |
| Middle Temperature | 249 to 282 | °C | |
| Front Temperature | 254 to 288 | °C | |
| Nozzle Temperature | 260 to 288 | °C | |
| Processing (Melt) Temp | 249 to 293 | °C | |
| Mold Temperature | 60.0 to 82.2 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Solprene® 1217 | Dynasol Elastomers | SBR, Solution | Solprene® |
| Adell Polyamide CR-16 | Adell Plastics, Inc. | Nylon, Unspecified | Adell Polyamide |
| LightSpan® LS2-6140 | NuSil Technology | Silicone | LightSpan® |
| LNP™ THERMOCOMP™ RC003 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ THERMOCOMP™ |
| OTECH PVC OF6625-Sandal | OTECH Corporation | PVC, Unspecified | OTECH PVC |