PLEXIGLAS® Sheet Solar 0Z023

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Industries AG
Trademark:	PLEXIGLAS® Sheet
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	QFfaZA_PLEXIGLAS-Sheet-Solar-0Z023.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

PLEXIGLAS® Solar 0Z023 is an extruded acrylic sheet material (polymethyl methacrylate, PMMA) that is highly weather-resistant and transparent.

Special Properties

UV transmission is specially adjusted to photovoltaics applications (PV, CPV),

providing better energy conversion efficiency and module efficiency, and

longer service life of photo cells, lenses and covers

Other Typical Properties

high mechanical strength, surface hardness and scratch resistance

ease of processing

good thermoformability

high heat deflection temperature

greater impact strength than glass combined with much lighter weight

Applications

Covers for build-in photovoltaics

Hot embossing of radial and linear Fresnel lenses for CPV/CSP applications

General Information
Features	Good Processability Good Weather Resistance High Hardness High Strength Scratch Resistant
Uses	Lenses Solar Panels
Appearance	Clear/Transparent
Forms	Sheet
Processing Method	Thermoforming

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Water Absorption - 24 h, 23°C ¹	38.0	mg	ISO 62

Flammability	Nominal Value		Test Method
Fire Rating	B2		DIN 4102

Additional Information	Nominal Value	Unit	Test Method
Weight Gain - during immersion ²	< 2.1	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	183	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3300	MPa	ISO 527-2/1
Tensile Stress (Break)	77.0	MPa	ISO 527-2/5
Tensile Strain (Break)	5.5	%	ISO 527-2/5

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	20	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	103	°C	ISO 75-2/B
1.8 MPa, Unannealed	98.0	°C	ISO 75-2/A
Vicat Softening Temperature	108	°C	ISO 306/B
CLTE - Flow (0 to 50°C)	8.0E-5	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.490		ISO 489
Transmittance ³	92.0	%	ISO 13468-2
Haze	< 0.50	%	ASTM D1003

Note Message
1 .	Method 1, specimen 60 x 60 x 2 mm³
2 .	Method 1
3 .	D65

Resin Grade	Manufacturer	Category	Trademark
Ultraform® S 2320 003 PRO	BASF Corporation	Acetal (POM) Copolymer	Ultraform®
Badadur® PBT8 GF/GK30	Bada AG	PBT	Badadur®
Alpha PVC GW 3040-LT NATURAL LCF	AlphaGary	PVC, Unspecified	Alpha PVC
Sylvin 83003-73 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Sylvin 916VO-95C Black	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin