TECHNYL® A 218G2 V50 BLACK 34N
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QFQwSh_TECHNYLA218G2V50BLACK34N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 218G2 V50 Black 34N is a polyamide 66, reinforced with 50% of glass fiber, heat stabilized, for injection moulding. This grade has been specially designed to improve its resistance to automotive cooling liquids, increasing lifetime of parts in permanent contact with such liquids. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.55 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 0.60 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 16200 | 12000 | MPa | ISO 527-2/1A |
| Tensile Stress (Break, 23°C) | 240 | 160 | MPa | ISO 527-2/1A |
| Tensile Strain (Break, 23°C) | 2.7 | 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 13500 | 10000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 350 | 270 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 95 | 97 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 260 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 255 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 262 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.8 mm | HB | -- | UL 94 | |
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.8 mm | 650 | -- | °C | IEC 60695-2-12 |
| 1.6 mm | 650 | -- | °C | IEC 60695-2-12 |
| 3.2 mm | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 290 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Mold Temperature | 70 - 100 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2740 S-90A | RTP Company | SEBS | RTP |
| Staramide 6 80E7 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| MonoSol® D-7031 XR | MonoSol, LLC | PVOH | MonoSol® |
| ADDINYL A2 ZV15 | ADDIPLAST | Nylon 66 | ADDINYL |
| MAJ'ECO DN080LA | AD majoris | Biodeg Polymers | MAJ'ECO |