Generic PP, High Crystal - Talc
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QFEU9q_Generic-PP-High-Crystal---Talc.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP, High Crystal - Talc This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 - 1.24 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.5 - 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.80 - 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 85 - 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 33.3 - 35.4 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 20 - 60 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1720 - 4510 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 34 - 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 115 - 150 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 60.0 - 65.0 | °C | |
| Injection Pressure | 63.7 - 78.5 | MPa | |
| Holding Pressure | 63.7 - 78.5 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP, High Crystal - TalcThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® ECO366 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Ultralloy™ 109 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| ACCUTECH™ CP0437C10L1 | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| LCA® N66-101 Type | UniPlas, Inc. | Nylon 66 | LCA® |
| Ixef® GS-1022 | Solvay Specialty Polymers | PARA | Ixef® |