VERSIFY™ 2300
| Category: | TPO (POE) , Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | VERSIFY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QEVoRC_VERSIFY-2300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VERSIFY™ 2300 Elastomer generates the optimum performance balance for blown stretch hoods - the wrapping that ensures the integrity of goods pallets being stored and transported. It provides excellent elasticity and good holding force at equal or better cost than competitor solutions. The film improves pallet stability, delivers better tear resistance and makes recycling and disposal much simpler. The grade is also ideally suited to a range of calendering and extruded applications and as a blend component for thermoplastic elastomers. Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.867 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Total Crystallinity | 13 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 1 | ASTM D2240 | ||
| Shore A, Compression Molded | 88 | ||
| Shore D, Compression Molded | 32 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 18.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 730 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 42.2 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -27.0 | °C | Internal Method |
| Vicat Softening Temperature | 43.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 66.0 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 20°, 1000 µm, Compression Molded | 70 | ||
| 60°, 1000 µm, Compression Molded | 109 | ||
| Haze (2000 µm, Injection Molded) | 6.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Hardness after 10 seconds. |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nipol® 1492P80 | Zeon Chemicals L.P. | NBR | Nipol® |
| Daelim Po1y® PP-333J | DAELIM INDUSTRIAL CO., LTD. | PP Random Copolymer | Daelim Po1y® |
| Hax™ HF 223F | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| KOPELEN SB-550A | Lotte Chemical Corporation | PP Terpolymer | KOPELEN |
| Moplen HP6057 | LyondellBasell Industries | PP Homopolymer | Moplen |