ALCUDIA® EVA PA-420-L
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® EVA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QDf6s1_ALCUDIA-EVA-PA-420-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EVA resin ALCUDIA® PA-420-L features low gel content and is recommended for extrusion coating applications, especially when high productions speeds are required. PA-420-L is also particularly suitable for co-extrusion with other polymers. It contains antioxidant and free flowing agent. TYPICAL APPLICATIONS Extrusion coating
Co-extrusion
PA-420-L is designed to be processed at temperatures as high as 220°C in high speed extrusion coating lines. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.940 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Vinyl Acetate Content | 20.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A | 84 | ||
| Shore D | 30 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 11.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 780 | % | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 53.0 | °C | ISO 306/A |
| Melting Temperature | 82.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 226F10 | SAX Polymers | Nylon 66 | SAXAMID™ |
| UMG ABS® VW100 | UMG ABS, Ltd. | ABS | UMG ABS® |
| EMPILON® 8879 | EMPILON | SEBS | EMPILON® |
| Hipolyene 8501 T6 B | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Kuraray Poval® PVA 220SB | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |