| Novamid® 1010CH ES is a Polyamide 6 (Nylon 6) material. It is available in Asia Pacific for injection molding. Primary attribute of Novamid® 1010CH ES: Low Viscosity. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.2 | -- | % | |
| Flow | 1.1 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.8 | -- | % | ISO 62 |
| Viscosity Number | 138 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3100 | -- | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 85.0 | -- | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 19 | -- | % | ISO 527-2 |
| Flexural Modulus | 2900 | -- | MPa | ISO 178 |
| Flexural Stress | 113 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.4 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 171 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 73.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 2.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 26 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.00 | -- | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.022 | -- | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 240 to 275 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5220 B78 | Spartech Polycom | PP, Unspecified | Spartech |
| MTEGRITY™ PS General Purpose GS230WC | M. Holland Company | PS (Specialty) | MTEGRITY™ PS General Purpose |
| VINIKA® CA88NA | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Hanwha Total PE R901U | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LLDPE | Hanwha Total PE |
| Plexiglas® V825 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |