Ferro PP TPP20AC06HB
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QCGqs6_Ferro-PP-TPP20AC06HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Primary end use is for AC/heater blower wheels. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.7 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 33.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 24 | % | ASTM D638 |
| Flexural Modulus | 2700 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 53.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 580 | J/m | ASTM D256 |
| Gardner Impact | 0.678 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 127 | °C | |
| 1.8 MPa, Unannealed | 72.0 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 204 to 210 | °C | |
| Middle Temperature | 210 to 213 | °C | |
| Front Temperature | 213 to 216 | °C | |
| Nozzle Temperature | 216 to 218 | °C | |
| Mold Temperature | 43.3 to 54.4 | °C | |
| Back Pressure | 0.138 to 0.345 | MPa | |
| Screw Speed | 100 to 150 | rpm | |
| Clamp Tonnage | 2.8 to 4.1 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2740 U-90A | RTP Company | SBS | RTP |
| DURANEX® 7407 | Polyplastics Co., Ltd. | PC+PBT | DURANEX® |
| Hylac® GP74 | Ravago Manufacturing Americas, LLC | ABS | Hylac® |
| SABIC® COHERE™ 8102 | Saudi Basic Industries Corporation (SABIC) | POP | SABIC® COHERE™ |
| Sylvin 9940-65 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |