3M™ Dyneon™ Fluoroelastomer FC 2144

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ Fluoroelastomer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	QC06Oh_3MDyneonFluoroelastomerFC2144.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
3M™ Dyneon™ Fluoroelastomer FC 2144 is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FC 2144 has an incorporated bisphenol cure system. Special Features Composition: dipolymer of vinylidene fluoride and hexafluoropropylene Medium viscosity Excellent release and hot tear properties essential for demoulding complex geometric profiles and parts containing severe undercuts Higher viscosity version of 3M™ Dyneon™ Fluoroelastomer FC 2123 Process targets: transfer and compression moulding, bonding and calendering Proprietary incorporated cure technology Typical Applications 3M™ Dyneon™ Fluoroelastomer FC 2144 is suitable for the manufacture of moulded goods and products which require a good bonding between rubber and metal.

Message

3M™ Dyneon™ Fluoroelastomer FC 2144 is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FC 2144 has an incorporated bisphenol cure system.

Special Features

Composition: dipolymer of vinylidene fluoride and hexafluoropropylene

Medium viscosity

Excellent release and hot tear properties essential for demoulding complex geometric profiles and parts containing severe undercuts

Higher viscosity version of 3M™ Dyneon™ Fluoroelastomer FC 2123

Process targets: transfer and compression moulding, bonding and calendering

Proprietary incorporated cure technology

Typical Applications
3M™ Dyneon™ Fluoroelastomer FC 2144 is suitable for the manufacture of moulded goods and products which require a good bonding between rubber and metal.

General Information
Features	Adhesiveness Good demoulding performance Medium viscosity
Uses	Bonding
Appearance	Opacity White-like
Forms	Thick sheet
Processing Method	Resin transfer molding Compression molding Calendering

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.80	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	41	MU	Internal method
Fluorine Content	66	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	70		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	4.20	MPa	ASTM D412A
Tensile Strength ²	17.0	MPa	ASTM D412A
Tensile Elongation ³(Break)	260	%	ASTM D412A
Compression Set			ASTM D1414
200°C, 70 hr ⁴	18	%	ASTM D1414
200°C, 70 hr ⁵	17	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould
4 .	Post cured 16 hours @ 230°C
5 .	Post cured 24 hours @ 260°C

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC M1496	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
BITONER® C9 H-120	Qingdao Bater Chemical Co., Ltd.	TP, Unspecified	BITONER®
Fiberfil® M-2501 BK	Fiberfil® Engineered Plastics Inc.	Nylon 66	Fiberfil®
Hifax CA 1168 G	LyondellBasell Industries	PP Impact Copolymer	Hifax
KOCETAL® GB705	Kolon Plastics, Inc.	Acetal (POM) Copolymer	KOCETAL®