DENILEN B 2010 CB
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Vamp Tech |
| Trademark: | DENILEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q8yTLL_DENILEN-B-2010-CB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP, 20% glass fiber reinforced, not Flame Retardant compound, good mechanical properties, chemically bonded. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.60 | % | |
| Across Flow | 0.90 | % | |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 65.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 11 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 140 | °C | ASTM D648A |
| Vicat Softening Temperature | 130 | °C | ASTM D1525 1 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 120 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 | °C | |
| Mold Temperature | 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Duroloy® AS-41 | Unigel Plásticos | PC+ABS | Duroloy® |
| Karina CLEAR PVC COMPOUND 74/203-D-IS-SI (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ RCL36S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| POLIGOM 04/AF | Crosspolimeri S.p.A. | TP, Unspecified | POLIGOM |
| TECACOMP® PA66 TC white 3923 | Ensinger GmbH | Nylon 66 | TECACOMP® |