VESTAMID® HTplus F1001
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® HTplus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q8vuuD_VESTAMID-HTplus-F1001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyphthalamide especially suitable for filaments. VESTAMID HTplus F1001 is based on a polyphthalamide (PPA). This special resin is specifically tailored for manufacturing monofilaments which can be subjected to high temperature. VESTAMID HTplus F1001 is supplied as spherical pellets in polyethylene packaging. Drying at 120°C for at least 4 hours before processing is recommended. For information about processing of VESTAMID HTplus, please follow the general recommendations for PPA in our brochure. Handling and Processing of VESTAMID HTplus." Furthermore our technical experts would appreciate to give support regarding the special requirements for producing filaments from VESTAMID HTplus F1001. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3700 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Break | 100 | MPa | ISO 527-2 |
| Break, 23°C, 0.370 mm 1 | > 300 | MPa | ISO 527-2/1, ISO 527-2/2 |
| Tensile Strain | |||
| Break | 3.0 | % | ISO 527-2 |
| Break, 23°C, 0.370 mm 2 | > 150 | % | ISO 527-2/1 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strain at Break (180°C, 3 hr, 0.370 mm) | > 150 | % | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 300 to 315 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr |
| Note Message | |
|---|---|
| 1 . | After extrusion |
| 2 . | After extrusion |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 300 HI2 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Karina BLACK PVC COMPOUND 75850-48/1-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucent PBT PBT-FR310 | Lucent Polymers, Inc. | PBT | Lucent PBT |
| PENTAMID AB GV25 MC25 H RC schwarz | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |
| Hifax TYC 2005P S62840 | LyondellBasell Industries | PP Copolymer | Hifax |