SureSpec HW50-001
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Genesis Polymers |
| Trademark: | SureSpec |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q7DGvG_SureSpec-HW50-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HW50-001 is a High Molecular Weight Hexene Copolymer certified prime resin developed for blown films. HW50-001 features UNIMODAL molecular weight distribution for improved processability at lower extruder pressure and good film stiffness. HW50-001 can be used alone or in BLENDS with LLDPE blown film grades and/or HMW-HDPE. HW50-001 can be used in a broad range of applications blended from 10% to 50% with either HMW-HDPE and/or LLDPE. HW50-001 can be processed on HMW, high stalk film equipment with a die gap >0.75 to 1.25< mm.. Recommended processing temperatures 195 to 205°C. HW50-001 complies with FDR regulation 21CFR 177.1520 (c) 3.1 (a) + 3.2 (a) and with most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | < 0.10 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 12 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 12 µm | 26.0 | MPa | |
| TD : Yield, 12 µm | 14.0 | MPa | |
| MD : Break, 12 µm | 61.0 | MPa | |
| TD : Break, 12 µm | 27.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 12 µm | 300 | % | |
| TD : Break, 12 µm | 410 | % | |
| Dart Drop Impact 1(12 µm) | 200 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 12 µm | 15 | g | |
| TD : 12 µm | 25 | g |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 195 to 205 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 CF 20 H | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| InnoTuf® TP-4007 | Innovative Polymers, Inc. | TSU | InnoTuf® |
| Karina BLACK PVC COMPOUND CAK 751-48/1-TEC-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina CLEAR PVC COMPOUND BTR-72/201-D-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petro Rabigh PP AV161 | Rabigh Refining & Petrochemical Co. | PP Impact Copolymer | Petro Rabigh PP |