Sicostirolo 684V0
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Ravago Group |
| Trademark: | Sicostirolo |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q5Urbv_Sicostirolo-684V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HIPS V0 flame retardant grade PBDE free |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 25.0 | MPa | |
| Break | 22.0 | MPa | |
| Tensile Strain (Break) | 30 | % | ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 8.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 81.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 98.0 | °C | ISO 306/A50 |
| -- | 90.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm, in Oil) | 50 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DINAPLEN® PPH1S20 M203-4106 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| Formolene® 6510A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| K-Prene SHEATHING EPR 5064 | Technovinyl Polymers India Ltd. | MPR | K-Prene |
| LTP ZC-2602 CF 30% | Chengdu Letian Plastics Co., Ltd | TP, Unspecified | LTP |
| Sylvin 6226-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |