Ultramid® Structure B3WG12 LFX BK23215
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q5Gb9f_UltramidStructureB3WG12LFXBK23215.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid Structure B3WG12 LFX BK23215 is a 60% long glass-fiber fiber reinforced and heat aging resistant injection molding grade designed for applications requiring excellent strength and stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.71 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.54 | -- | % | ISO 294-4 |
| Flow | 0.24 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 20800 | 14200 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 260 | 170 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | 2.4 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 19500 | 14700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 410 | 280 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 42 | 41 | kJ/m² | ISO 179 |
| 23°C | 41 | 36 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 91 | 83 | kJ/m² | ISO 179 |
| 23°C | 92 | 88 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 80 - 100 | °C | |
| Injection Pressure | 3.50 - 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Impax 450 | Primex Plastics Corporation | PS (HIPS) | Prime Impax |
| Sinvicomp SIM5520 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| TAROMID B 280 G5 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| Ebalta HFG plus / PUR 11 | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| Karina ORANGE PVC COMP. -E 850-32/ 72-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |