LNP™ THERMOCOMP™ LF003 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q4eYaZ_LNP-THERMOCOMP-LF003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP LF003 is a compound based on Polyetheretherketone resin containing 15% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound LF-1003 Product reorder name: LF003 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.79 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6930 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 137 | MPa | ASTM D638 |
| Yield | 125 | MPa | ISO 527-2 |
| Break | 137 | MPa | ASTM D638 |
| Break | 125 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.9 | % | ASTM D638 |
| Yield | 2.4 | % | ISO 527-2 |
| Break | 3.1 | % | ASTM D638 |
| Break | 2.4 | % | ISO 527-2 |
| Flexural Modulus | 7000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 200 | MPa | ASTM D790 |
| -- | 209 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 1 | 6.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 850 | J/m | ASTM D4812 |
| 23°C 2 | 54 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 14.6 | J | ASTM D3763 |
| -- | 3.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 329 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 3 | 325 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 259 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 244 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 4.9E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.8E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP HM5303W | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Axiall PVC 10753 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| DOMAMID® 6G25 | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| DOMAMID® AQ 500 | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| KOCETAL® WR303BK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |