KOPA® KN333G50
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q3Q6Yw_KOPAKN333G50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPA®KN333G50 is a polyamide 66 (nylon 66) product, which contains a 50% glass fiber reinforced material. It can be processed by injection molding and is available in North America, Latin America, Europe or Asia Pacific. KOPA®KN333G50 applications include electrical/electronic applications, engineering/industrial accessories and the automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.58 | g/cm³ | ASTM D792 |
| -- | 1.56 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 - 0.40 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 230 | MPa | ASTM D638 |
| 23°C | 250 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.0 | % | ASTM D638 |
| Fracture, 23°C | 2.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 13200 | MPa | ASTM D790 |
| 23°C | 13000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 353 | MPa | ASTM D790 |
| 23°C | 360 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 18 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 252 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 250 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 255 | °C | ISO 75-2/A |
| Melting Temperature | 255 | °C | ISO 11357-3 |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Arc Resistance | 135 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80 - 100 | °C | |
| Drying Time - Desiccant Dryer | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 290 | °C | |
| Front Temperature | 295 | °C | |
| Nozzle Temperature | 300 | °C | |
| Mold Temperature | 60 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3490 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RAMSTER PF300G9 | Polyram Ram-On Industries | PBT | RAMSTER |
| DENILUB Y 20G 4TF | Vamp Tech | Nylon 66 | DENILUB |
| Edgetek™ CY4000 BK006 | PolyOne Corporation | PC+PBT | Edgetek™ |
| PADMEX 56035 | Pemex Petroquímica | HDPE | PADMEX |