SOLLAMID B 2700 FV 25
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Krisoll Resinas Plásticas Ltda. |
| Trademark: | SOLLAMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q3FPQb_SOLLAMID-B-2700-FV-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SOLLAMID B 2700 FV 25 is a Polyamide 6 (Nylon 6) material filled with 25% glass fiber. It is available in Latin America. Primary attribute of SOLLAMID B 2700 FV 25: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.32 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.35 to 0.55 | -- | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.0 | -- | % | ASTM D570 |
| Heat Stability | 100 to 110 | -- | °C |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 122 | 110 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 7000 | 4500 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 135 | 85.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.5 | 5.5 | % | ASTM D638 |
| Flexural Modulus (23°C) | 6500 | 4000 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 210 | 120 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 9.0 | 15 | kJ/m² | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 195 | -- | °C | |
| 1.8 MPa, Unannealed | 180 | -- | °C | |
| Melting Temperature | 214 to 220 | -- | °C | |
| CLTE - Flow | 3.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | Notch B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 8.4.0 | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |
| Zythane® 7090AF | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| ASACOM™ S5000 | Polymer Compounders Limited | ASA | ASACOM™ |
| Generic Polyester, TS | Generic | Polyester, TS | Generic |
| Karina WHITE PVC COMPOUND 806-10/236-H-ISE-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |