TECHNYL® C 246SI V30 NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q37GLa_TECHNYL-C-246SI-V30-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, reinforced with 30 % of glass fibre, with high impact resistance, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | ||||
| Across Flow | 0.84 | -- | % | ISO 294-4 |
| Across Flow | 0.46 | -- | % | Internal Method |
| Flow | 0.39 | -- | % | Internal Method |
| Flow | 0.33 | -- | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.88 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.840 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8300 | 4900 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 140 | 90.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 4.5 | 10 | % | ISO 527-2/1A |
| Flexural Modulus | 7220 | -- | MPa | ISO 178 |
| Flexural Stress | 220 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -- | 23 | 36 | kJ/m² | |
| -30°C | 15 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -- | 92 | -- | kJ/m² | |
| -30°C | 100 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 250 to 280 | °C | |
| Middle Temperature | 250 to 280 | °C | |
| Front Temperature | 260 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 HS TFE 15 | RTP Company | Nylon 66 | RTP |
| Shanghai Potomer SG8 | Shanghai Potomer International Trade Co., Ltd. | PVC, Rigid | Shanghai Potomer |
| Unipren® Elastomers A3 NTLA010 70A UP303 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| ACCUTECH™ NY0730G20L1 | ACLO Compounders Inc. | Nylon 6 | ACCUTECH™ |
| Sylvin 8826-65FUV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |