Nypol® PA A3 G30 HS AML0254 NR429
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q1OH8A_Nypol-PA-A3-G30-HS-AML0254-NR429.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 in color yellow reinforced with 30% of fiberglass, term stabilized. Good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 to 1.38 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| Saturation | 6.0 | -- | % | |
| Equilibrium | 1.9 | -- | % | |
| Ash Content | 28 to 32 | -- | % | ASTM D2584 |
| Relative Viscosity - Formic Acid | 46.0 to 52.0 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9700 | 7000 | MPa | ASTM D638 |
| Tensile Strength | 200 | 135 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.2 | 5.0 | % | ASTM D638 |
| Flexural Modulus | 12200 | 6500 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | -- | 70 | kJ/m² | |
| 23°C | > 70 | > 70 | kJ/m² | |
| Notched Izod Impact (Area) (23°C) | 11.0 | 14.0 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact (Area) | ASTM D256 | |||
| -30°C | -- | 70.0 | kJ/m² | |
| 23°C | > 70.0 | > 70.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 260 | -- | °C | |
| 1.8 MPa, Unannealed | 250 | -- | °C | |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 270 to 285 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRILOY® 200FT | Samyang Corporation | PC+ABS | TRILOY® |
| 4PROP® 2C11110 | 4Plas | PP Copolymer | 4PROP® |
| Diakon® CLG356L | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| FRIANYL® A3 GF25 V0P2 | Nilit Plastics | Nylon 66 | FRIANYL® |
| Elastocon® 2865ST | Elastocon TPE Technologies | TPE | Elastocon® |