TRIBOCOMP® POM CF10 TS0
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q10h7E_TRIBOCOMP-POM-CF10-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TRIBOCOMP®POM CF10 TS0 is a polyoxymethylene (POM) copolymer product, which contains 10% ptfe fiber and 10% carbon fiber reinforced materials. It is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.70 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 6500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 95.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | ||
| Dynamic | 0.13 | ASTM D3702 | |
| Static | 0.12 | ASTM D3702 | |
| Wear Factor | 12.0 | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 165 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 160 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 4.0E-5 | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.37 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 160 - 210 | °C | |
| Middle Temperature | 170 - 220 | °C | |
| Front Temperature | 180 - 220 | °C | |
| Nozzle Temperature | 200 - 225 | °C | |
| Processing (Melt) Temp | < 220 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205B TFE 15 FR | RTP Company | Nylon 610 | RTP |
| RTP 800 MS 3 | RTP Company | Acetal (POM) Copolymer | RTP |
| SUPREME Specialty PS SP263 | Supreme Petrochem Ltd. | PS (Specialty) | SUPREME Specialty PS |
| Bashplast Compound SSP-A17 (BP)/CB-B25 (BP) | Bashplast Ltd. | PE, Unspecified | Bashplast Compound |
| Arnitel® EL740-H/A | DSM Engineering Plastics | TPC-ET | Arnitel® |