Order Products : sales@su-jiao.com
MAJORIS DG304E/8 - 9432
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q0SVwU_MAJORIS-DG304E-8---9432.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DG304E/8 - 9432 is a 33% chemically coupled glass fiber reinforced polyethylene high density compound (pellets length ~8 mm) intended for injection moulding. APPLICATIONS DG304E/8 - 9432 is intended for components that require good impact strength, rigidity and dimensional stability. Suitable applications are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.20 - 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 69.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 4500 | MPa | ISO 178 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 44 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 127 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 115 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 - 200 | °C | |
| Processing (Melt) Temp | 190 - 230 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALGLASS H 15 S 30 G | RIALTI Srl | PP Homopolymer | RIALGLASS |
| RJM SD101G20-G | RJM International, Inc. | PC | RJM |
| TEREZ PA 6 7510 GF 15 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Trithene® CX 7065 | Petroquimica Triunfo | LDPE | Trithene® |
| HiFill® PA6/6 LGF60 HS L UV 12mm | Techmer Engineered Solutions | Nylon 66 | HiFill® |