Hostacom TRC 377N
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PzeVw3_Hostacom-TRC-377N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom TRC 377N is a mineral filled high impact, high stiffness polypropylene copolymer. The grade has been specifically designed for moulding large complex parts that require good impact as well as good stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.75 to 0.90 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | > 70 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 19.5 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | > 80 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 1750 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | > 2.0 | kJ/m² | |
| 23°C | > 20 | kJ/m² |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michital G1200 | API Polymers, Inc. | Acetal (POM) Copolymer | Michital |
| SCHULABLEND® (PC/ASA) WR 5 SHI SF | A. Schulman Europe | ASA+PC | SCHULABLEND® |
| UBESTA 3030 JLX8 | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Expandable PS D833B | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| VALOX™ ENH4565 resin | SABIC Innovative Plastics Asia Pacific | PBT | VALOX™ |