OMIKRON KRT 705 NERO 808
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | TECNOPOL |
| Trademark: | OMIKRON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PyZFmY_OMIKRON-KRT-705-NERO-808.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OMIKRON KRT 705 E is a copolymer polypropylene filled with 30% of talc for injection moulding, high workibility. It is available iblack version, coloured on demand. Omikron KRT 705 E has a good thermal and U.V. stabilisation. OMIKRON KRT 705 is suitable for moulding of items requiring a good balance between impact and stiffness well as good aesthetic. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 19.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 20 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| 0°C | 4.0 | kJ/m² | ISO 180 |
| 23°C | 9.0 | kJ/m² | ISO 180 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Aging (150°C) | 6.3 | day | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 62.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 63.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 210 - 240 | °C | |
| Middle Temperature | 210 - 240 | °C | |
| Front Temperature | 210 - 240 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Pressure | 9.00 - 11.0 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.500 - 1.00 | MPa |
| Injection instructions |
|---|
| Post Pressure: 60 - 80 bar |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® BIO 35LANF30-0.101 | Transmare Compounding B.V. | PLA | TRANSMARE® BIO |
| Fainplast PVC MPH 80 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Hostacom TRC 483N C12827 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Lotader® AX 8840 | Arkema | EMA | Lotader® |
| OnForce™ LFT LF0100-5002 NATURAL | PolyOne Corporation | PUR, Unspecified | OnForce™ LFT |