Ingeo™ 3260HP
| Category: | PLA , Polylactic Acid |
| Manufacturer: | NatureWorks® LLC |
| Trademark: | Ingeo™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PyOYMI_Ingeo3260HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ingeo 3260HP is a low viscosity product from NatureWorks, designed for high flow injection molding applications. It is designed to crystallize during processing, leading to higher heat deflection temperatures in opaque applications. The variety of products made with 3260HP is widely varied and growing. Applications include disposables such as cutlery, cups, plates, cosmetic packaging, and durables such as electronics housings. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 65 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | |||
| -- 1 | 0.20 - 0.40 | % | |
| -- 2 | 1.7 - 1.8 | % | |
| Relative Viscosity 3(30°C) | 2.50 | ASTM D5225 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 4(Yield) | 63.4 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Fracture 5 | 3.0 | % | ASTM D638 |
| Fracture 6 | 1.3 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| -- 7 | 3590 | MPa | ASTM D790 |
| -- 8 | 4300 | MPa | ASTM D790 |
| Flexural Strength 9 | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 10 | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM E2092 | ||
| 0.45 MPa, not annealed 11 | 56.0 | °C | ASTM E2092 |
| 0.45 MPa, not annealed 12 | 151 | °C | ASTM E2092 |
| Peak Crystallization Temperature (DSC) 13 | 165 - 180 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.025 | % | |
| Rear Temperature | 175 | °C | |
| Middle Temperature | 185 | °C | |
| Front Temperature | 190 | °C | |
| Nozzle Temperature | 190 | °C | |
| Processing (Melt) Temp | 199 | °C | |
| Mold Temperature | 120 | °C | |
| Back Pressure | 1.72 | MPa | |
| Screw Speed | 200 | rpm |
| Note Message | |
|---|---|
| 1 . | Amorphous, 26°C Mold Temperature |
| 2 . | Crystalline, 120°C Mold Temperature |
| 3 . | 1.0 g/dL in chloroform |
| 4 . | Amorphous, 26°C Mold Temperature |
| 5 . | Amorphous, 26°C Mold Temperature |
| 6 . | Crystalline, 120°C Mold Temperature |
| 7 . | Amorphous, 26°C Mold Temperature |
| 8 . | Crystalline, 120°C Mold Temperature |
| 9 . | Amorphous, 26°C Mold Temperature |
| 10 . | Amorphous, 26°C Mold Temperature |
| 11 . | Amorphous, 26°C Mold Temperature |
| 12 . | Crystalline, 120°C Mold Temperature |
| 13 . | Crystalline, 120°C Mold Temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoPrene 67A-1000 | KMI Group Inc. | TPV | PrimoPrene |
| Vipel® F701-FHG-00 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| AMTOPP PL30 | Inteplast Group | PP, Unspecified | AMTOPP |
| Hydrin® T5010 | Zeon Chemicals L.P. | Epoxy | Hydrin® |
| KEBAFORM® C 901 TF | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |