U-polymer L-8005
| Category: | Polyarylate , Polyarylate |
| Manufacturer: | UNITIKA Plastics Division |
| Trademark: | U-polymer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PwMvdd_U-polymer-L-8005.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| U Series Resin Composite Grade |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.00 mm) | 0.80 | % | ASTM D955 |
| Water Absorption (24 hr, 3.18 mm) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 64.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 85 | % | ASTM D638 |
| Flexural Modulus | 2500 | MPa | ASTM D790 |
| Flexural Strength | 99.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 110 | °C | ASTM D648 |
| CLTE - Flow | 6.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 40 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.015 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Additional Information |
|---|
| Coefficient of Dynamic Coefficient: 02 to 0.3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren N110 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| U-polymer AXF-1500-05 | UNITIKA Plastics Division | Polyarylate | U-polymer |
| Daelim Po1y® LH-402 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Geon™ Vinyl Flexible XV3878G | PolyOne Corporation | PVC+NBR | Geon™ Vinyl Flexible |
| Electrafil® PA6 GF20 | Techmer Engineered Solutions | Nylon 6 | Electrafil® |